The effect of CO2 9.3 μm short-pulsed laser irradiation in enamel erosion reduction with and without fluoride applications—a randomized, controlled in vitro study

C. V. Silva & T. F. Mantilla & Y. Engel & J. P. Tavares & P. M. Freitas & P. Rechmann

Click here for full study.

ABSTRACT

The aim of this in vitro study was to evaluate the protective effect of short-pulsed CO2 9.3 μm laser irradiation against erosion in human enamel without and combined with TiF4 and AmF/NaF/SnCl2 applications, respectively, as well as compared to the protective effect of these fluoride treatments alone. After polishing, ninety enamel samples (3 × 3mm) were used for 9 different treatment groups: 4% TiF4 gel (pH 1.5, 24,533 ppm F−); AmF/NaF/SnCl2 rinse (pH 4.5; 500 ppm F−, 800 ppm Sn2); CO2 laser (average power 0.58 W); CO2 laser (0.58 W) + TiF4; CO2 laser (0.58 W) + AmF/NaF/SnCl2; CO2 laser (0.69 W); CO2 laser (0.69W) + TiF4; CO2 laser (0.69 W) + AmF/NaF/SnCl2; negative control (deionized water). TiF4 gel was brushed on only once before the first erosive cycling, while samples treated with AmF/NaF/SnCl2 were daily immersed in 5 ml of the solution before cycling. Laser treatment occurred with a CO2 laser (wavelength 9.3 μm, pulse repetition rate 100 Hz, pulse duration 14.6 μs/ 18 μs, average power 0.58 W/0.69 W, fluence 1.9 J/cm2/2.2 J/cm2, beam diameter 0.63 mm, irradiation time 10 s, air cooling). TiF4 was applied only once, whileAmF/NaF/SnCl2 was applied once daily before the erosive challenge. Surface loss (in μm) was measured with optical profilometry immediately after treatment, and after 5 and 10 days of erosive cycling (0.5% citric acid, pH 2.3, 6 × 2 min/day). Additionally, scanning electron microscopy investigations were performed. All application measures resulted in loss of surface height immediately after treatment. After 5 days, significantly reduced surface loss was observed after applying laser irradiation (both power settings) followed by applications of TiF4 or AmF/NaF/SnCl2 solution (p < 0.05; 2-way ANOVA and Tukey test) compared to fluoride application alone. After 10 days, compared to after 5 days, a reduced tissue loss was observed in all groups treated with AmF/NaF/SnCl2 solution. This tissue gain occurredwith the AmF/NaF/SnCl2 application alone and was significantly higher when the application was combined with the laser use (p < 0.05). Short-pulsed CO2 9.3 μm laser irradiation followed by additional application of AmF/NaF/SnCl2 solution significantly reduces the progression of dental enamel erosion in vitro.

Case Report of Spongiotic Gingivitis in an Adult Male T...

Eugenia P. Roberts, DDS Gregory M. Schuster, DDS Steven Haub, DDS

1 min read

Request More Information